Material properties of bulk hydrophobic concrete in a Nordic environment

By: Language: English Summary language: Swedish Series: TRITA-ABE-DLT ; 2312Publication details: Stockholm : KTH Royal Institute of Technology, 2023Description: 101 sISBN:
  • 9789180405201
Subject(s): Online resources: Notes: Härtill 3 uppsatser Dissertation note: Lic.-avh. (sammanfattning) Stockholm : Kungliga Tekniska högskolan, 2023 Summary: Concrete in its unaltered form allows the mass transfer of fluids into and out of its microstructure. These fluids can contain detrimental solutes which change the chemistry of the cement paste and/or the corrosion properties of the reinforcement bars, most noticeably hydrogen carbonates (HCO3 -), oxygen (O2) and chloride ions (Cl-). Water and its solutions containing salts, mostly sodium chloride (NaCl), can also cause physical damage due to phase changes (freezing and thawing). External application of hydrophobic agents onto the cement paste surface is a well-known method to alter the mass transfer at this interface. Bulk application of hydrophobic agents in ready mixed concrete is also a possible route but alters the entire cement paste. This thesis presents relevant aspects concerning the use of bulk hydrophobic agents in concrete within a spectrum water to cement ratio (w/c) = 0.40-0.50. The main focus was on triacylglycerides (TAG) and alkyl alkoxysilanes (“silanes”) with application rates 1-3% based on cement weight. A field test station close to vehicular traffic was also established in 2018 and 2019, but the specimens have not been tested at this point in time.Summary: Betong i sin oförändrade form tillåter masstransport av vätskor i och ur dess mikrostruktur. Dessa vätskor kan innehålla skadliga lösta ämnen som förändrar cementpastans kemi och/eller korrosionsegenskaperna hos armeringsjärnen, framför allt vätekarbonater (HCO3-), syre (O2) och kloridjoner (Cl-). Vatten och dess lösningar som innehåller salter, mestadels natriumklorider (NaCl), kan till och med orsaka fysisk skada på grund av fasförändringar (frysning och upptining). Extern applicering av hydrofoba medel på cementpastans yta är en välkänd metod för att ändra masstransport genom denna gränsyta. Bulkapplicering av hydrofoba medel i färdigblandad betong är också en möjlig väg, och resulterar i förändringar i hela cementpastan. Denna licentiatavhandling presenterar relevanta aspekter rörande användningen av bulk-hydrofoba medel i betong inom intervall av vattencementtal = 0,40-0,50 (vct). Huvudfokus låg på triacylglyceroler (TAG) och alkyl-alkoxisilaner (”silaner”) med inblandning 1-3 % baserat på cementvikt. En fältteststation intill fordonstrafik etablerades också 2018 och 2019 men provkropparna har inte testats vid denna tidpunkt.
Item type: Licentiate thesis
No physical items for this record

Härtill 3 uppsatser

Lic.-avh. (sammanfattning) Stockholm : Kungliga Tekniska högskolan, 2023

Concrete in its unaltered form allows the mass transfer of fluids into and out of its microstructure. These fluids can contain detrimental solutes which change the chemistry of the cement paste and/or the corrosion properties of the reinforcement bars, most noticeably hydrogen carbonates (HCO3 -), oxygen (O2) and chloride ions (Cl-). Water and its solutions containing salts, mostly sodium chloride (NaCl), can also cause physical damage due to phase changes (freezing and thawing). External application of hydrophobic agents onto the cement paste surface is a well-known method to alter the mass transfer at this interface. Bulk application of hydrophobic agents in ready mixed concrete is also a possible route but alters the entire cement paste. This thesis presents relevant aspects concerning the use of bulk hydrophobic agents in concrete within a spectrum water to cement ratio (w/c) = 0.40-0.50. The main focus was on triacylglycerides (TAG) and alkyl alkoxysilanes (“silanes”) with application rates 1-3% based on cement weight. A field test station close to vehicular traffic was also established in 2018 and 2019, but the specimens have not been tested at this point in time.

Betong i sin oförändrade form tillåter masstransport av vätskor i och ur dess mikrostruktur. Dessa vätskor kan innehålla skadliga lösta ämnen som förändrar cementpastans kemi och/eller korrosionsegenskaperna hos armeringsjärnen, framför allt vätekarbonater (HCO3-), syre (O2) och kloridjoner (Cl-). Vatten och dess lösningar som innehåller salter, mestadels natriumklorider (NaCl), kan till och med orsaka fysisk skada på grund av fasförändringar (frysning och upptining). Extern applicering av hydrofoba medel på cementpastans yta är en välkänd metod för att ändra masstransport genom denna gränsyta. Bulkapplicering av hydrofoba medel i färdigblandad betong är också en möjlig väg, och resulterar i förändringar i hela cementpastan. Denna licentiatavhandling presenterar relevanta aspekter rörande användningen av bulk-hydrofoba medel i betong inom intervall av vattencementtal = 0,40-0,50 (vct). Huvudfokus låg på triacylglyceroler (TAG) och alkyl-alkoxisilaner (”silaner”) med inblandning 1-3 % baserat på cementvikt. En fältteststation intill fordonstrafik etablerades också 2018 och 2019 men provkropparna har inte testats vid denna tidpunkt.